Microhardness of ?ompacted thermally expanded graphite
DOI:
https://doi.org/10.17721/1812-5409.2019/1.40Анотація
Using the method of continuous microindentation with different loading on the indenter, the microhardness of compacted thermo-expanded graphite (TEG) samples of different dispersion was studied. The analysis of the obtained results showed that, with an increase in the average cross-sectional area of TEG particles from 40 to 120 microns, the microhardness of the samples under investigation also increases. An analysis of the influence of the dispersion and morphology of the TEG particles on the distribution of microhardness on the surface of the compacted samples of TEG was also carried out. The microhardness indicatrix for the samples of the original TEG shows that when the radial displacement from the center of the sample, the microhardness of the material decreases. So in the central part of the discoid sample the values of microhardness lie in the range from 0,04 to 0,025 GPa. In the next concentric region, the microhardness decreases by 30% and gains a value of (0.028 ... 0.014) GPA. When the dispersion of TEG particles changes, the distribution of microhardness also changes. The microhardness indicatrix for a compacted Tg sample with an average particle size of 180 ?m shows that the microhardness value at the center of the sample ranges from 0.065 to 0.15 GPa.As you approach the edge of the sample, the microhardness of the material decreases from 0.15 to 0.054 GPa. The study of TEG with an average particle size of 50 ?m showed that the indentation in the center and in the middle region of the sample gives an isotropic distribution of microhardness values. The microhardness values coincide in the central and middle regions of the sample and correspond to ? 0.1 GPa. The proposed method of research and analysis of microhardness on the surface of compacted specimens of TEG gives an opportunity not only to characterize the micromechanical properties of the investigated material but also to optimize the technological regimes for obtaining samples.
Key words: micromechanical properties, graphite, microhardness, thermo-expanded graphite.
Pages of the article in the issue: 174-177
Language of the article: Ukrainian
Посилання
SEMENTSOV YU.I, REVO S.L, IVANENKO K.O. (2016) Thermally exfoliated graphite. Kyiv: Interservis.
AVRAMENKO T.G., KHUTORYANSKAYA N.V., MIKHALYUK O.V. et al. (2016) Structure and sorption characteristics of nanoporous carbon materials. Surf Eng Appl Elect. 52(4). р. 313-318.
REVO S.L, BUDZULYAK I.M., RACHIY B.I., and KUZISHIN M.M. (2013) Electrode Material for Supercapacitors Based on Nanostructured Carbon. Surf Eng Appl Elect. 49(1). p. 68-72.
MIYOSHI K. (2002) Surface characterization techniques: an overview. NASA/TM 2002- 211497, Glenn Research Center of NASA. p. 45.
Завантаження
Номер
Розділ
Ліцензія
Автори, роботи яких публікуються у цьому журналі, погоджуються з такими умовами:
- Автори зберігають авторські права та надають журналу право на першу публікацію роботи, яка одночасно ліцензується згідно із Creative Commons Attribution License, тобто надається дозвіл іншим ділитися роботою з визнанням авторства роботи та першої публікації в цьому журналі.
- Автори можуть укладати окремі додаткові угоди щодо невиключного розповсюдження опублікованої журналом версії роботи (наприклад, розмістити її у репозитарії наукової установи чи опублікувати у книзі) з підтвердженням її початкової публікації у цьому журналі.
- Дозволяється та заохочується розміщення своїх робіт в мережі Інтернет авторами (наприклад, у репозитаріях наукових установ або на особистих веб-сторінках) до та під час процесу подання, оскільки це може призвести до продуктивного обміну, а також до більш ранніх цитувань опублікованої роботи та їх більшої кількості (див. The Effect of Open Access).