Physico-mechanical characteristics of nanocomposite materials based on fluoroplastic
DOI:
https://doi.org/10.17721/1812-5409.2021/3.20Ключові слова:
нанокомпозиційний матеріал, мікротвердість, політрифторхлоретилен, розширений графітАнотація
In this work, the elastic and strength properties of polymer composites with a polytrifluorochlorethylene matrix and a thermally expanded graphite filler were evaluated by the nanoindentation method, and the effect of the dispersion and concentration of the filler on the mechanical characteristics of nanocomposite materials was considered. It is shown that the microhardness of nanocomposite materials decreases with increasing filler concentration. An increase in the microhardness and Young's modulus with the growth of filler particles was observed for nanocomposite materials with a filler concentration of 3 vol.%. As for nanocomposite materials with a filler volume fraction of 10 vol.%, similar behavior of the mechanical characteristics was observed with an increase in the dispersion of thermally expanded graphite particles to 180 ?m. A subsequent increase in the average particle size of thermally expanded graphite leads to a decrease in Young's modulus and microhardness of composites, which may be associated with different degrees of polymer structuring and the formation of different orientational orders from the filler. The observed changes in Young's modulus and H/E ratio indicate a change in the amorphous crystalline behavior of the composite to that characteristic of fine-crystalline materials and depends on the dispersion of thermally expanded graphite.
Pages of the article in the issue: 107 - 110
Language of the article: Ukrainian
Посилання
JOSE J.P., THOMAS S., KURUVILLA J., MALHOTRA S.K., GODA K., M.S. SREEKALA M.S. (2012) Advances in polymer composites: Macro- and microcomposites—State of the art, new challenges, and opportunities. Polymer Composites, Wiley. 1. pp. 3–16.
MASUELLI M.A. (2013) Introduction of fibre-reinforced polymers–Polymers and composites: Concepts, properties and processes. Fiber Reinforced Polymers–The Technology Applied for Concrete Repair; M. Masuelli, Ed. p. 39.
LIN S., ANWER M.A.S., ZHOU Y., SINHA A., CARSON L., NAGUIB H. (2018) Evaluation of the thermal, mechanical and dynamic mechanical characteristics of modified graphite nanoplatelets and graphene oxide high-density polyethylene composites. Composites Part B: Engineering. 132. pp. 61–68.
SEMENTSOV YU.I., REVO S.L., IVANENKO K.O. (2016) Thermally exfoliated graphite. Kyiv: Interservis.
PANDA A., DYADYURA K., VAL͡CEK J., HARNIˇCÁROV M., ZAJAC J., MODRÁ V., PANDOV I., VRÁBEL P., NOVÁKOVÁ-MARCINˇCÍNOV E. AND PAVELEK Z. (2017) Manufacturing Technology of Composite Materials–Principles of Modification of Polymer Composite Materials Technology Based on Polytetrafluoroethylene. Materials. 10(4). p. 377.
Завантаження
Опубліковано
Номер
Розділ
Ліцензія
Автори, роботи яких публікуються у цьому журналі, погоджуються з такими умовами:
- Автори зберігають авторські права та надають журналу право на першу публікацію роботи, яка одночасно ліцензується згідно із Creative Commons Attribution License, тобто надається дозвіл іншим ділитися роботою з визнанням авторства роботи та першої публікації в цьому журналі.
- Автори можуть укладати окремі додаткові угоди щодо невиключного розповсюдження опублікованої журналом версії роботи (наприклад, розмістити її у репозитарії наукової установи чи опублікувати у книзі) з підтвердженням її початкової публікації у цьому журналі.
- Дозволяється та заохочується розміщення своїх робіт в мережі Інтернет авторами (наприклад, у репозитаріях наукових установ або на особистих веб-сторінках) до та під час процесу подання, оскільки це може призвести до продуктивного обміну, а також до більш ранніх цитувань опублікованої роботи та їх більшої кількості (див. The Effect of Open Access).