Self-organized Au-GaAs metal-semiconductor micro- and nanostructures for applications in plasmonic photovoltaics

I. M. Dmitruk; Nataliya I. Berezovska; K. O. Maiko; S. V. Mamykin; I. B. Mamontova

doi:10.17721/1812-5409.2021/3.26

Authors

I. M. Dmitruk Taras Shevchenko National University of Kyiv
Nataliya I. Berezovska Taras Shevchenko National University of Kyiv https://orcid.org/0000-0002-6967-6426
K. O. Maiko Taras Shevchenko National University of Kyiv https://orcid.org/0000-0002-2035-1284
S. V. Mamykin V.Ye. Lashkaryov Institute for Physics of Semiconductors, NAS of Ukraine, 03028, Kyiv, Nauky Prospect, 45 https://orcid.org/0000-0002-9427-324X
I. B. Mamontova V.Ye. Lashkaryov Institute for Physics of Semiconductors, NAS of Ukraine, 03028, Kyiv, Nauky Prospect, 45 https://orcid.org/0000-0003-0368-3065

DOI:

https://doi.org/10.17721/1812-5409.2021/3.26

Keywords:

solar cell, gallium arsenide, nanoparticle, surface plasmon

Abstract

Au-GaAs metal-semiconductor composite microstructures have been prepared by an anisotropic etching of n-GaAs (100) wafers doped with Te (10¹⁶ to 10¹⁷ cm^-3) with subsequent photostimulated chemical deposition of noble metal (Au) on formed semiconductor quasigratings. The microrelief topology of GaAs surface is controlled by the anisotropic etching conditions. Au metal was deposited on the structured GaAs surface as randomly placed nanoparticles of various shape and size and/or nanowires on the top of the hills of formed semiconductor microstructure. As the number of Au nanoparticles increases, they tend to localize on the ledges of the GaAs microrelief forming a system of approximately parallel nanowires. Obtained periodic structures with submicron to microns periods without Au nanoparticles and with deposited nanoparticles have been studied by means of scanning electron microscopy, optical spectroscopy (photoluminescence spectroscopy at room temperature), and photoelectric measurements. The decrease of the relative intensity of main photoluminescence band for samples with Au nanostructures compared to ones without nanoparticles deposition and simultaniously changes of the shape of photocurrent spectra of Au-GaAs microstructures have been observed. Such correlation in behaviour of measured spectra make formed Au-GaA metal-semiconductor microstructures perspective for the application in plasmonic photovoltaics.

Pages of the article in the issue: 139 - 142

Language of the article: English

References

DOU, B., JIA, R., XING, Z., YAO, X., XIAO, D., Z. Jin, & LIU, X. (2021) Enhanced Performance of Nanotextured Silicon Solar Cells with Excellent Light-Trapping Properties. Photonics. 8(7). p. 272.

SPINELLI, P., FERRY, V.E., VAN de GROEP, J., VAN LARE, M., VERSCHUUREN, M.A., SCHROPP, R.E.I., ATWATER, H.A. & POLMAN, A. (2012) Plasmonic light trapping in thin-film Si solar cells. Journal of Optics. 14 (2). p. 024002.

ENRICHI, F., QUANDT, A. & RIGHINI, G. C. (2018) Plasmonic enhanced solar cells: Summary of possible strategies and recent results. Renewable and Sustainable Energy Reviews. 82 (3). p. 2433-2439.

PAPEZ, N., DALLAEV, R., ŢALU, S. & KASTYL, J. (2021) Overview of the Current State of Gallium Arsenide-Based Solar Cells. Materials. 14 (11). p. 3075.

DMITRUK, N.L., BORKOVSKAYA, O.Yu., MAMONTOVA, I.B., MAMYKIN, S.V., MALYNYCH, S.Z. & ROMANYUK, V.R. (2015) Metal nanoparticle-enhanced photocurrent in GaAs photovoltaic structures with microtextured interfaces. Nanoscale Research Lett. 10. p. 72.

LIU, X., JIA, L., FAN, G., GOU, J., LIU, S.F. & YAN, B. (2016) Au nanoparticle enhanced thin-film silicon solar cells. Solar Energy Materials and Solar Cells. 147. p. 225-234.

BEREZOVSKA N., DMITRUK, I., KALYUZHNYY, A., DMYTRUK, A. & BLONSKYI, I. (2018) Self-Organized Structuring of Surface of Metal-Semiconductor Composite by Femtosecond Laser Processing. Ukrainian Journal of Physics. 63 (5). p. 406-412.